| PROPERTY | UNIT | VALUE / RANGE |
| Melting Point | °C | 265 - 267 |
| Density | g mL-1 | 1.71 - 1.73 |
| Coefficient of Thermal Expansion | cm / (cm °C) | |
| Heat Deflection Temperature, 0.5 MPa | °C | |
| Heat Deflection Temperature, 1.8 MPa | °C | |
| Thermal Conductivity x 10-5 | W / mK | |
| Rockwell Hardness, D Scale | n/a | D66 - D67 |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | 22.9 - 26 |
| Tensile Strength, Break at 23 C | MPa | 45 - 51 |
| Elongation, Yield | % | 200 - 375 |
| Elongation, Break | % | 425 |
| Tensile Modulus at 23 C | MPa | 840- 1150 |
| Flexural Strength, Yield | MPa | |
| Flexural Modulus | MPa | 1000 - 1380 |
| Compressive Strength | MPa | |
| Izod Notched | J / m | |
| Izod Unnotched | J / m | No Break |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | ||
| Dielectric Strength | V/mm x 104 | 5.9 | |
| Dielectric Constant @ 1 MHz | n/a | 2.47 - 2.58 | |
| Dissipation Factor @ 1 MHz | n/a, x 10-4 | 55 |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | ||
| Mold Shrinkage | % | ||
| Continuous Service Temperature | °C | 150 - 155 | |
| Water Absorption, 24 hr. Immersion | % | 0.03 - 0.11 |